Fe76Si7.6B9.5P5C1.9薄膜的纵向驱动巨磁阻抗效应The Longitudinally Driven Giant Magneto-Impedance Effect of Fe76Si7.6B9.5P5C1.9 Films
作者:
褚光, 方允樟, 何兴伟, 马云, 李文忠
关键字:
巨磁阻抗效应, 薄膜, 纵向驱动, 灵敏度Giant Magneto-Impedance Effect; Film; Longitudinally Driven; Sensitivity
期刊名称:
《Advances in Condensed Matter Physics》, Vol.2 No.1, 2013-02-17
摘要:
采用磁控溅射方法制备了单层Fe76Si7.6B9.5P5C1.9薄膜,利用HP4294A型阻抗分析仪测量了经过不同温度退火3.0μm厚的FeSiBPC薄膜的纵向驱动巨磁阻抗效应。实验结果表明:经250℃退火的薄膜样品在190 kHz驱动频率下的最大巨磁阻抗比为157.32%,外场灵敏度为1.55%/(A∙m−1)。
Fe76Si7.6B9.5P5C1.9 single-layer films were prepared by magnetron sputtering. An HP4294Aimpedance ana- lyzer was used to measure the curves of longitudinally driven giant magneto-impedance. Films with3.0mm thickness were annealed under different temperatures. The results showed that at a driven frequency of 190 kHz for the samples annealed at 250˚C, the maximum giant magneto-impedance effect of the samples with thickness of 3.0 μm is 157.32%. And the sensitivity of it is 1.55%/(A∙m−1).