J. F. Lin, K. W. Chen, J. Q. Xie, et al. Effect of implantation temperature and volume flow rate ratio of nitrogen and hydrogen on nitrogen concentration distribution, mechanical properties, fatigue life, fracture toughness, and tribological behavior of plasma-nitrided P20, 718 and 420 steels. Surface and Coatings Technology, 2007, 201(12): 5912-5924.
被以下文章引用:
-
标题:
Cr4Mo4V钢等离子体基碳氮离子升温注渗层微观结构Microstructure of Carbonitrided Layer of Cr4Mo4V Steel Treated by Plasma-Based Ion Implantation at Elevated Temperature
作者:
马欣新, 李忠文, 赵开礼, 唐光泽
关键字:
Cr4Mo4V钢, 碳氮等离子体基升温注渗, 显微结构Cr4Mo4V Steel; PBII Carbonitriding; Microstructure
期刊名称:
《Material Sciences》, Vol.2 No.3, 2012-07-26
摘要:
本文采用XRD、SEM、TEM和HRTEM等方法表征了Cr4Mo4V钢升温碳氮离子注渗层的微观结构，结果表明升温注渗处理层中生成了铁的碳化物和氮化铬析出相，析出相弥散分布于晶内和晶界。马氏体发生细化，原始板条马氏体边界消失，形成了微晶、微孪晶和细小片层等结构。HRTEM在马氏体中观察到非晶区和层错等亚结构。
XRD, SEM, TEM and HRTEM are used to investigate the microstructure of Cr4Mo4V steel after Plasma- base ion implantation (PBII) carbonitriding treatment. The results indicate the carbide and chromium nitride phases precipitate in the carbonitrided layer within the grain or along grain boundary. The grain refining and boundary disap- pearing in initial martensite occur. The micro-crystal, micro-twin and micro-lath martensite structure are observed. The substructure of amorphous zones and stacking faults are found by HRTEM.