标题:
铁基合金的纵向驱动非对称巨磁阻抗效应The Longitudinally Driven Asymmetric Giant Magneto-Impedance Effect in Fe-Based Alloy
作者:
杨光, 何兴伟, 范晓珍, 周初凯, 赵静, 王红洲, 肖飞, 方允樟
关键字:
电流退火, 巨磁阻抗效应, 非对称性Current Annealing; GMI Effect; Asymmetry
期刊名称:
《Advances in Condensed Matter Physics》, Vol.3 No.1, 2014-02-12
摘要:
研究了直流电流退火的Fe73.5Cu1Nb3Si13.5B9合金薄带的巨磁阻抗效应,实验发现,经0.72 A电流退火10 min后,样品巨磁阻抗比有最大值1810.4%。经0.74 A电流退火10 min后,样品由于自身存在偏置场,其巨磁阻抗效应开始出现零磁场的非对称现象,结合XRD图谱分析表明,样品非对称巨磁阻抗效应的产生与B6-Fe23硬磁相的析出有关。
We have investigated the giant magneto-impedance effect ofFe73.5Cu1Nb3Si13.5B9 alloy ribbons which were annealed by DC current. It was found that the maximum GMI ratio was 1810.43% after 10-min annealing current of 0.72 A. However, the GMI effect began to show asymmetric phenomenon around zero magnetic field after 10-min annealing current of 0.74 A in terms of its own existence bias field. XRD spectrum analysis indicated that the B6-Fe23 hard magnetic phase precipitated should be responsible for the asymmetric giant magneto-impedance effect.