MS  >> Vol. 3 No. 1 (January 2013)

    Sn含量对银钎料焊接性的影响
    Effect of Sn Content on Brazing Properties of Ag Based Filler Alloy

  • 全文下载: PDF(3974KB) HTML   XML   PP.16-21   DOI: 10.12677/MS.2013.31004  
  • 下载量: 3,461  浏览量: 9,949  

作者:  

王晓蓉,余丁坤,贺艳明,黄世盛,陈 融:杭州华光焊接新材料股份有限公司研发中心

关键词:
银钎料Sn含量显微组织力学性能Ag Based Filler Alloy; Sn Content; Microstructure; Mechanical Properties

摘要:

通过往Ag-Cu-Zn系钎料内添加适量的SnNi元素,利用OMSEMXRD研究了钎料内Sn含量对钎料组织与焊接性能的影响。结果表明:Ag-Cu-Zn系钎料内主要成分为:Ag基固溶体;Cu基固溶体;CuZn化合物;当Sn含量达到4 wt%时,出现少量的Ag2Cu2O化合物。在本研究设计的成分范围内,钎料内并未出现Cu-Sn金属间化合物。差热分析表明:随着Sn含量的增加,钎料的固液相线温度均出现不同程度的下降。润湿试验表明:相同的加热温度下,不同Sn含量的银钎料均可对不锈钢形成良好的润湿。此外,采用该系列钎料手工火焰钎焊了不锈钢与不锈钢,得到的接头内母材/钎料界面处形成了致密的连接,无缺陷存在;当Sn含量为3.0 wt%时,得到接头的最高拉伸强度达到了450 MPa;当Sn含量超过3.0 wt%时,由于钎料内少量氧化物的存在使接头性能出现大幅度下降。

Sn and Ni element were introduced into Ag-Cu-Zn filler alloy, and the effect of Sn content on microstructure and brazing properties of Ag based filler alloy was analyzed by OM, SEM and XRD. The results indicated that the Ag-Cu-Zn filler alloy was mainly comprised of Ag based solid solution, Cu based solid solution and CuZn compounds. A trace amount of Ag2Cu2O occurred in the filler alloy while the content of Sn exceeded 4 wt% in the filler. However, the Cu-Sn intermetallics were not detected in the range of composition in the research. By using DSC analysis, the melting temperature of the filler alloy was decreased with increasing Sn content. The wettability test showed that the stainless steel could be wetted by the Ag-Cu-Zn based filler alloy with different Sn content. Besides, this kind of filler alloy was used to join stainless steel by torch brazing, and a compact bonding could be obtained at the substrates/filler alloy interface. The maximum joint strength could reach 450 MPa while the filler contained 3.0 wt% Sn element. While the content of Sn exceeded 3.0 wt% in the filler, the joint strength decreased sharply due to the existence of few oxides.

文章引用:
王晓蓉, 余丁坤, 贺艳明, 黄世盛, 陈融. Sn含量对银钎料焊接性的影响[J]. 材料科学, 2013, 3(1): 16-21. http://dx.doi.org/10.12677/MS.2013.31004

参考文献

[1] 李卓然, 刘彬, 冯吉才. 含银20%的银基无镉中温钎料配方的优化设计[J]. 焊接学报, 2008, 29(8): 5-8.
[2] J. L. Wiese. Strength of metal-to-metal brazed joints. MIT, 2000: 30-35.
[3] 王星平, 赖忠民, 薛松柏, 张亮, 卢方焱. 合金元素对Ag-Cu- Zn系钎料影响的研究现状及发展趋势[J]. 电焊机, 2009, 39(11): 1-6.
[4] 甘卫平, 陈慧, 杨伏良. Ag-Cu-In-Sn 钎料加工工艺的研究[J]. 材料导报, 2007, 21(3): 156-158.
[5] 卢方焱, 薛松柏, 赖忠民, 张亮, 顾立勇, 顾文华. 镓对Ag- CuZn钎料组织和性能的影响[J]. 焊接学报, 2009, 30(1): 56-59.
[6] 赖忠民, 薛松柏, 张亮, 皋利利, 顾立勇, 顾文华. Ag-Cu-Zn- Sn-xGa-yIn钎料性能与显微组织[J]. 焊接学报, 2010, 31(3): 73-76.
[7] 韩宪鹏. 镓对无镉银钎料性能影响的研究[D]. 南京航空航天大学, 2008: 11-13.
[8] 崎诚三, 平林真, 刘安生. 二元合金状态图籍[M]. 北京: 冶金工业出版社, 2004.
[9] 矫宁. 新型低银无镉中温钎料组织与性能的研究[D]. 哈尔滨工业大学, 2007: 30-36.
[10] 赖忠民. Ga/In与稀土Ce对Ag30CuZnSn钎料显微组织及钎焊接头性能影响的研究[D]. 南京航空航天大学, 2011.